Factors affecting setting:Following

Factors affecting setting:
Following are the factors that affect the setting of concrete.

1. Water Cement ratio
2. Suitable Temperature
3. Cement content
4. Type of Cement
5. Fineness of Cement
6. Relative Humidity
7. Admixtures
8. Type and amount of Aggregate



2. Workability of Concrete
Workability is often referred to as the ease with which a concrete can be transported, placed and consolidated without excessive bleeding or segregation.

OR

The internal work done required to overcome the frictional forces between concrete ingredients for full compaction. It is obvious that no single test can evaluate all these factors. In fact, most of these cannot be easily assessed even though some standard tests have been established to evaluate them under specific conditions.

In the case of concrete, consistence is sometimes taken to mean the degree of wetness; within limits, wet concretes are more workable than dry concrete, but concrete of same consistence may vary in workability.

Because the strength of concrete is adversely and significantly affected by the presence of voids in the compacted mass, it is vital to achieve a maximum possible density. This requires sufficient workability for virtually full compaction to be possible using a reasonable amount of work under the given conditions. Presence of voids in concrete reduces the density and greatly reduces the strength: 5% of voids can lower the strength by as much as 30%.

Slump Test can be used to find out the workability of concrete. View Procedure of Slump Test

Factors affecting concrete workability:
Water-Cement ratio
Amount and type of Aggregate
Amount and type of Cement
Weather conditions
Temperature
Wind
Chemical Admixtures
Sand to Aggregate ratio
i. Water content or Water Cement Ratio
More the water cement ratio more will be workability of concrete. Since by simply adding water the inter particle lubrication is increased. High water content results in a higher fluidity and greater workability but reduces the strength of concrete. Because with increasing w/c ratio the strength decreases as more water will result in higher concrete porosity. So, the lower the w/c, the lower is the void volume/solid volume, and the stronger the hardened cement paste. Related ArticleAlso See: Rate of Strength Gain of Concrete

Increased water content also results in bleeding, hence, increased water content can also mean that cement slurry will escape through the joints of the formwork (Shuttering).

ii. Amount and type of Aggregate
Since larger Aggregate sizes have relatively smaller surface areas (for the cement paste to coat) and since less water means less cement, it is often said that one should use the largest practicable Aggregate size and the stiffest practical mix. Most building elements are constructed with a maximum Aggregate size of 3/4" to 1", larger sizes beingprohibited by the closeness of the reinforcing bars. Related ArticleAlso See: Effects of Different Aggregates on Properties of Concrete

Because concrete is continuously shrinking for years after it is initially placed, it is generally accepted that under thermal loading it will never expand to it's originally-placed volume. More the amount of aggregate less will be workability.

Using smooth and round aggregate increases the workability. Workability reduces if angular and rough aggregate is used.

Greater size of Aggregate- less water is required to lubricate it, the extra water is available for workability

Angular aggregates increases flakiness or elongation thus reduces workability. Round smooth aggregates require less water and less lubricationand gretaer workability in a given w/c ratio

Porous aggregates require more water compared to non absorbent aggregates for achieving sam degree of workability.
iii. Aggregate Cement ratio
More ratio, less workability. Since less cement mean less water, so the paste is stiff.

iv. Weather Conditions
1. Temperature
If temperature is high, evaporation increases, thus workability decreases.

2. Wind:
If wind is moving with greater velocity, the rate of evaporation also increase reduces the amount of water and ultimately reducing workability.



v. Admixtures
Chemical admixtures can be used to increase workability.

Use of air entraining agent produces air bubbles which acts as a sort of ball bearing between particles and increases mobility, workability and decreases bleeding, segregation. The use of fine pozzolanic materials also have better lubricating effect and more workability.

vi. Sand to Aggregate ratio
If the amount of sand is more the workability will reduce because sand has more surface area and more contact area causing more resistance. The ingredients of concrete can be proportioned by weight or volume. the goal is to provide the desired strength and workability at minimum expense. A low water-cement ratio is used to achieve a stronger concrete. It would seem theref

Results (Malay) 1:

Faktor-faktor yang mempengaruhi persekitaran:Berikut adalah faktor-faktor yang mempengaruhi persekitaran yang konkrit.1. air simen nisbah 2. sesuai suhu 3. kandungan simen 4. jenis-jenis simen 5. kehalusan simen 6. kelembapan 7. campuran 8. jenis dan jumlah agregat 2. kebolehkerjaan konkritKebolehkerjaan sering dirujuk sebagai kemudahan yang konkrit yang boleh dibawa, diletakkan dan disatukan tanpa pendarahan berlebihan atau pengasingan.ATAUKerja-kerja dalaman yang dilakukan perlu mengatasi kuasa-kuasa geseran antara bahan-bahan konkrit untuk pemadatan penuh. Ia adalah jelas bahawa tiada ujian boleh menilai semua faktor di atas. Malah, sebahagian besar ini tidak mudah dinilai walaupun beberapa ujian standard telah ditubuhkan untuk menilai mereka di bawah syarat-syarat tertentu.Dalam kes konkrit, konsistensi, kadang-kadang diambil untuk bermaksud tahap basah; dalam had, konkrit yang basah adalah lebih boleh dilaksanakan daripada konkrit Kering, tetapi konkrit konsistensi yang sama mungkin berbeza-beza dalam kebolehkerjaan.Kerana kekuatan konkrit adalah negatif dan signifikan dipengaruhi oleh kehadiran lompang dalam jisim dipadatkan, ia adalah penting untuk mencapai ketumpatan maksimum mungkin. Ini memerlukan kebolehkerjaan yang mencukupi untuk pemadatan hampir penuh boleh menggunakan jumlah yang munasabah kerja di bawah syarat-syarat yang diberikan. Kehadiran lompang dalam konkrit mengurangkan ketumpatan dan sangat mengurangkan kekuatan: 5% daripada lompang boleh mengurangkan kekuatan sebanyak 30%.Slump Test can be used to find out the workability of concrete. View Procedure of Slump TestFactors affecting concrete workability:Water-Cement ratioAmount and type of AggregateAmount and type of CementWeather conditionsTemperatureWindChemical AdmixturesSand to Aggregate ratioi. Water content or Water Cement RatioMore the water cement ratio more will be workability of concrete. Since by simply adding water the inter particle lubrication is increased. High water content results in a higher fluidity and greater workability but reduces the strength of concrete. Because with increasing w/c ratio the strength decreases as more water will result in higher concrete porosity. So, the lower the w/c, the lower is the void volume/solid volume, and the stronger the hardened cement paste. Related ArticleAlso See: Rate of Strength Gain of ConcreteIncreased water content also results in bleeding, hence, increased water content can also mean that cement slurry will escape through the joints of the formwork (Shuttering).ii. Amount and type of AggregateSince larger Aggregate sizes have relatively smaller surface areas (for the cement paste to coat) and since less water means less cement, it is often said that one should use the largest practicable Aggregate size and the stiffest practical mix. Most building elements are constructed with a maximum Aggregate size of 3/4" to 1", larger sizes beingprohibited by the closeness of the reinforcing bars. Related ArticleAlso See: Effects of Different Aggregates on Properties of ConcreteKerana konkrit mengecut secara berterusan selama bertahun-tahun selepas ia pada mulanya diletakkan, ia umumnya diterima bahawa di bawah terma yang memuatkan ia akan tidak pernah berkembang ia diletakkan pada asalnya jumlah. Lebih banyak jumlah agregat kurang akan kebolehkerjaan.Menggunakan agregat halus dan bulat meningkatkan kebolehkerjaan yang. Kebolehkerjaan mengurangkan jika agregat sudut dan kasar digunakan.Lebih besar saiz agregat kurang air diperlukan untuk melincirkan ia, air tambahan terdapat kebolehkerjaanSudut agregat kenaikan penyerpihan atau elongation sekali gus mengurangkan kebolehkerjaan. Agregat halus bulat memerlukan air kurang dan kurang kebolehkerjaan gretaer lubricationand w/c nisbah yang diberikanAgregat berliang memerlukan lebih banyak air berbanding bebas penyerap agregat untuk mencapai darjah kebolehkerjaan sam.iii. agregat nisbah simenLebih banyak nisbah, tolak nombor. Oleh kerana kurang simen maksud kurang air, jadi paste adalah sengit.iv. cuaca1. suhuJika suhu tinggi, penyejatan meningkat, sekali gus kebolehkerjaan berkurangan.2. angin:Jika angin yang bergerak dengan halaju yang lebih besar, kadar penyejatan juga meningkatkan mengurangkan jumlah air dan akhirnya mengurangkan kebolehkerjaan. v. campuranCampuran bahan kimia boleh digunakan bagi meningkatkan kebolehkerjaan.Penggunaan agen entraining udara menghasilkan buih udara yang bertindak sebagai sejenis bebola galas antara zarah-zarah dan meningkatkan mobiliti, kebolehkerjaan dan pendarahan, penurunan pengasingan. Penggunaan bahan-bahan pozzolanic yang baik juga mempunyai pelincir lebih baik kesan dan kebolehkerjaan yang lebih banyak.vi. Sand to Aggregate ratioIf the amount of sand is more the workability will reduce because sand has more surface area and more contact area causing more resistance. The ingredients of concrete can be proportioned by weight or volume. the goal is to provide the desired strength and workability at minimum expense. A low water-cement ratio is used to achieve a stronger concrete. It would seem theref

Results (Malay) 2:

Faktor yang mempengaruhi persekitaran:
Berikut adalah faktor-faktor yang mempengaruhi penetapan konkrit. 1. Nisbah Cement air 2. Sesuai suhu 3. Kandungan simen 4. Jenis Simen 5. Kehalusan Simen 6. Kelembapan relatif 7. Bahan tambah 8. Jenis dan jumlah agregat 2. Kebolehkerjaan konkrit kebolehkerjaan sering dirujuk sebagai meringankan dengan yang konkrit yang boleh diangkut, diletakkan dan disatukan tanpa pendarahan berlebihan atau pengasingan. ATAU Kerja-kerja dalaman selesai diperlukan untuk mengatasi daya geseran antara bahan-bahan konkrit untuk pemadatan penuh. Ia adalah jelas bahawa tiada ujian tunggal boleh menilai semua faktor-faktor ini. Malah, sebahagian besar tidak boleh dengan mudah dinilai walaupun beberapa ujian standard telah ditubuhkan untuk menilai mereka di bawah syarat-syarat tertentu. Dalam kes konkrit, konsisten kadang-kadang diambil untuk bermaksud tahap kelembapan; dalam had, konkrit basah adalah lebih terperinci dan efektif daripada konkrit kering, tetapi konkrit konsisten sama mungkin berbeza dari segi kebolehkerjaan. Kerana kekuatan konkrit adalah buruk dan dengan ketara dipengaruhi oleh kehadiran lompang dalam jisim dipadatkan, ia adalah penting untuk mencapai maksimum ketumpatan. Ini memerlukan kebolehkerjaan yang mencukupi untuk pemadatan hampir penuh menjadi mungkin menggunakan jumlah yang munasabah kerja di bawah syarat-syarat yang diberikan. Kehadiran lompang dalam konkrit mengurangkan ketumpatan dan sangat mengurangkan kekuatan: 5% lompang boleh mengurangkan kekuatan sebanyak 30%. Slump Test boleh digunakan untuk mengetahui kebolehkerjaan konkrit. Lihat Tatacara Slump Test Faktor yang mempengaruhi kebolehkerjaan konkrit: air-simen nisbah Jumlah dan jenis agregat Jumlah dan jenis Cement Keadaan cuaca suhu Wind Chemical bahan tambah Sand untuk agregat nisbah i. Kandungan air atau Nisbah Cement Air Lebih nisbah air simen lebih akan kebolehkerjaan konkrit. Sejak dengan hanya menambah air pelinciran zarah antara bertambah. Keputusan kandungan air yang tinggi dalam sifat berubah-ubah yang lebih tinggi dan kebolehkerjaan yang lebih besar tetapi mengurangkan kekuatan konkrit. Kerana dengan peningkatan w / c nisbah kekuatan berkurangan kerana air lebih akan menyebabkan keliangan konkrit yang lebih tinggi. Jadi, lebih rendah w / c, yang lebih rendah adalah jumlah yang tidak sah / jumlah pepejal, dan kuat pes simen keras itu. Berkaitan ArticleAlso Lihat: Kadar Kekuatan Gain Konkrit kandungan air yang meningkat juga menyebabkan pendarahan, dengan itu, meningkatkan kandungan air boleh juga bermakna bahawa buburan simen akan melarikan diri melalui sendi acuan (Shuttering) itu. Ii. Jumlah dan jenis agregat Sejak saiz agregat yang lebih besar mempunyai kawasan permukaan yang agak kecil (untuk adunan simen untuk kot) dan sejak kurang air bermakna simen kurang, ia sering berkata bahawa seseorang itu perlu menggunakan saiz agregat dilaksanakan terbesar dan campuran praktikal stiffest. Kebanyakan elemen bangunan dibina dengan saiz agregat maksimum 3/4 "ke 1", saiz yang lebih besar beingprohibited oleh keakraban bar memperkukuh. Berkaitan ArticleAlso Lihat: Kesan Agregat yang berbeza pada Properties of Concrete Kerana konkrit terus mengecut selama bertahun-tahun selepas ia pada mulanya diletakkan, ia diterima secara umum bahawa di bawah pembebanan haba ia tidak akan berkembang ke ia jumlah asalnya tangga. Lebih jumlah agregat kurang akan kebolehkerjaan. Menggunakan agregat halus dan bulat meningkatkan kebolehkerjaan. Kebolehkerjaan mengurangkan jika agregat sudut dan kasar digunakan. Saiz Greater air Aggregate- kurang diperlukan untuk melincirkan ia, air tambahan disediakan untuk kebolehkerjaan agregat sudut meningkatkan penyerpihan atau pemanjangan itu mengurangkan kebolehkerjaan. Round agregat halus memerlukan kurang air dan kurang lubricationand kebolehkerjaan gretaer dalam tertentu w / c nisbah agregat berliang memerlukan lebih banyak air berbanding dengan agregat bukan penyerap untuk mencapai ijazah sam kebolehkerjaan. Iii. Cement nisbah agregat Lebih nisbah, kurang kebolehkerjaan. Sejak simen kurang bermakna kurang air, jadi pes adalah sengit. Iv. Keadaan Cuaca 1. Suhu Jika suhu adalah tinggi, penyejatan meningkat, dengan itu kebolehkerjaan berkurangan. 2. ANGIN: . Jika angin bergerak dengan halaju yang lebih besar, kadar penyejatan juga meningkatkan mengurangkan jumlah air dan akhirnya mengurangkan kebolehkerjaan v. Bahan tambah bahan tambah kimia boleh digunakan untuk meningkatkan kebolehkerjaan. Gunakan ejen entraining udara menghasilkan gelembung udara yang bertindak sebagai satu bentuk bebola galas antara zarah dan meningkatkan mobiliti, kebolehkerjaan dan mengurangkan pendarahan, pengasingan. Penggunaan bahan-bahan pozzolanic halus juga mempunyai kesan pelincir yang lebih baik dan lebih kebolehkerjaan. Vi. Pasir kepada nisbah agregat Jika jumlah pasir adalah lebih kebolehkerjaan akan mengurangkan kerana pasir mempunyai luas permukaan yang lebih dan banyak lagi kawasan sentuhan menyebabkan rintangan lagi. Bahan-bahan konkrit boleh manis mengikut berat dan sukatan. matlamatnya adalah untuk memberi kekuatan yang dikehendaki dan kebolehkerjaan dengan perbelanjaan minimum. Nisbah air-simen yang rendah digunakan untuk mencapai konkrit yang lebih kukuh. Ia akan kelihatan seolah theref