Typically, 1000 mg of ESO and 600 m

Typically, 1000 mg of ESO and 600 mg of LA were charged
in a reactor that contained a stirrer bar. The reactor was
purged with nitrogen for roughly 15 min to remove the air
and then was sealed. Put the reactor on a 90
C hot plate
with a magnetic stirring at 300 rpm. The reaction was
allowed to continue for 6 h. The final reaction mixture was
washed with water to remove unreacted chemicals till the
pH value of the washing solution turns to 7.0, and the
desired product lactic acid-epoxidized soybean oil (LA-ESO)
was recovered by evaporating the water off under reduced
pressure. Generally, 1190 mg of product was obtained.
Around 2.1 epoxy groups per ESO molecule were opened by
LA, and the conversion rate of epoxy group was 70%

Results (Vietnamese) 2:

Thông thường, 1000 mg của ESO và 600 mg của LA bị buộc tội
trong một lò phản ứng có chứa một thanh khuấy. Các lò phản ứng đã được
làm sạch bằng nitơ cho khoảng 15 phút để loại bỏ không khí
và sau đó đã được niêm phong. Đặt lò phản ứng trên một tấm nóng 90 ° C
với khuấy từ 300 rpm. Phản ứng được
phép tiếp tục trong 6 giờ. Hỗn hợp phản ứng cuối cùng đã được
rửa sạch bằng nước để loại bỏ hóa chất không phản ứng cho đến khi
giá trị pH của dung dịch rửa hóa đến 7.0, và các
sản phẩm mong muốn lactic acid-epoxy hóa dầu đậu nành (LA-ESO)
đã được phục hồi bằng cách làm bay hơi nước ra dưới giảm
áp lực. Nói chung, 1190 mg sản phẩm thu được.
Khoảng 2,1 nhóm epoxy mỗi phân tử ESO được mở ra bởi
LA, và tỷ lệ chuyển đổi của nhóm epoxy là? 70%